The influence of iodide on glass transition temperature of high‐pressure nuclear waste glasses

Résumé

The glass transition temperature (Tg) is a key parameter to investigate for application in nuclear waste immobilization in borosilicate glasses. Tg for several glasses containing iodine (I) has been measured in order to determine the I effect on Tg. Two series of glass composition (ISG and NH) containing up to 2.5 mol% I and synthesized under high pressure (0.5 to 1.5 GPa) have been investigated using differential scanning calorimetry (DSC). The I local environment in glasses has been determined using X‐ray photoelectron spectroscopy and revealed that I is dissolved under its iodide form (I−). Results show that Tg is decreased with the I addition in the glass in agreement with previous results. We also observed that this Tg decrease is a strong function of glass composition. For NH, 2.5 mol% I induces a decrease of 24°C in Tg, whereas for ISG, 1.2 mol% decreases the Tg by 64°C. We interpret this difference as the result of the I dissolution mechanism and its effect on the polymerization of the boron network. The I dissolution in ISG is accompanied by a depolymerization of the boron network, whereas it is the opposite in NH. Although ISG corresponds to a standardized glass, for the particular case of I immobilization it appears less adequate than NH considering that the decrease in Tg for NH is small in comparison to ISG.
Fichier principal
Vignette du fichier
Glass transition of I-bearing borosilicate glasses vf_onefile-1.pdf (789.61 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03052155 , version 1 (15-12-2020)

Identifiants

Citer

Valentin Jolivet, Yann Morizet, Jonathan Hamon, Michael Paris, Tomo Suzuki-Muresan. The influence of iodide on glass transition temperature of high‐pressure nuclear waste glasses. Journal of the American Ceramic Society, 2021, 104 (3), pp.1360-1369. ⟨10.1111/jace.17571⟩. ⟨hal-03052155⟩
85 Consultations
188 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More